Compute the elongation, in %, of a cylindrical copper rod if it is cold worked such that the diameter is reduced from 15.9 mm to 10.4 mm Yield strength (psi x 10³)120100806040200110201040 Steel130 40Percent cold workBrass:Copper8007006005004003002001001150 60 70field strength (MPa)Tensile strength (psix 10³)14012010080604001020 - 301040 Steel40Percent cold work150BrassCopper90060 70800700600-500400300200Tensile strength (MPa)uDuctility (%EL)70605040201000Brass1040 SteelI10Copper20130 40Percent cold work506070

Answered: Compute the elongation, in %, of a…

Compute the elongation, in %, of a cylindrical copper rod if it is cold worked such that the diameter is reduced from 15.9 mm to 10.4 mm

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

The fluctuating stresses listed in the table are found at a critical location of a component made of steel with Se = 40 ksi, Sy = 80 ksi, Sut = 110 ksi and f= 0.87. These stresses are applied on the part within 10 s. What is the accumulative damage of this part? What is the life of the part in hours if this stress pattern continues to repeat for the remained of the part's life? Use Goodman criterion and Miner's rule in your solution. Loading order |Omin o max |Number of cycles -20 30 -10 50 1 3. -30 30 1
Tensile engineering stress-strain curves through failure are depicted below. Which specimen features the highest toughness? Engineering Stress, MPa 1800- 1600- 1400- 1200- 1000- 800- 600- 400- 200- Ol 0 Aluminum Alloy 2024-T81 0.04 0.08 Stainless Steel (18-8) 1340 Steel, Water-Quenched & Tempered at 370 C Magnesium 0.12 Structural Steel (Mild Steel) Engineering Strain 0.16 1340 Steel, Water-Quenched & Tempered at 370°C Aluminum Alloy 2024-T81 Structural Steel (Mild Steel) Stainless Steel (18-8) Magnesium 0.20 0.24
A cylindrical specimen of cold-worked steel has a Brinell hardness of 240. If the specimen remained cylindrical during deformation and its original radius was 10.4 mm, determine its radius after deformation. For steel, the dependence of tensile strength on percent cold work is shown in Animated Figure 7.19b. i mm
An S-N plot from fatigue testing of a steel is provided below. Use the plot to determine the following values for this steel. 1. Fatigue limit: 2. Fatigue lifetime at a stress amplitude of: 415 MPa: 275 MPa: 3. Fatigue strength at: 5x104 cycles: 5x105 cycles 500 400 300 200 100 0 1.E+04 Stress Amplitude (MPa) 1.E+05 1.E+06 Cycles to Failure 1.E+07 1.E+08
Given: Stress strain curve of 10 mm diameter and 1 m long ductile stainless-steel rod. 900 800 700 600 500 Mild 400 Stainless 300 200 - 100 0.1 0.2 0.3 0.4 Strain 0.5 0.6 0.7 Draw stress-strain curve for compression here 1. Label all points of significance on the stress strain curve 2. Draw the stress-strain curve for the rod in compression and label all points of significance. 3. What is the Young's modulus in tension? Assume .001 strain at 500 MPa 4. What is its Youngʻs modulus in compression? 5. What is the tensile yield strength of this rod using the 0.2% offset criteria? 6. What is the compressive yield strength of the rod? 7. What is force required to yield the rod?. Show calculation: 8. What is the UTS of this rod?. 9. What is the force required to break the rod? Show calculation: 10. What will be UCS of the rod? Stress (MPa)
4. Based on Figure 1 shows, for a carbon steel, the partial tensile engineering stress-strain curve. Determine; (i) Yield strength (o) (ii) Ultimate Tensile Strength (oTs) (ii) Young Modulus (E) 300 2000 10° psi 300 MPa 2000 200 200 1000 1000 100 100 0.000 0.005 0.010 Strain 0.015 0.000 0.020 0.040 0.060 0.080 Strain Figure 1: Engineering stress-strain curve for alloy steel Stress (MPa) Stress Stress (10° psi)
70% + | 8 0 4. An application requires ultimate tensile strength and yield strength of a steel at 110 ksi and 91 ksi, respectively. A data table is attached in the back of the test. Answer the following 4 questions: 4.1. Can SAE 1040 steel be selected for this application? 4.2. If "no" is the answer in Part I, the following Part II, III, and IV can be ignored. If "yes" is the answer in Part I, which condition of SAE 1040 should be selected? 4.3. Why is that steel with the condition in part II selected? 4.4. Is the selected steel brittle or ductile? and Why? Page 4 of 6
Cyclic Stresses (Fatigue); The S-N Curve 4. The fatigue data for a ductile cast iron are given as follows: Cycles to Failure Stress Amplitude [MPa (ksi)] 248 (36.0) 236 (34.2) 224 (32.5) 213 (30.9) 201 (29.1) 193 (28.0) 193 (28.0) 193 (28.0) 1 × 105 3 x 105 1 x 10⁰ 3 x 106 1 x 107 3 x 107 1 108 3 × 108 (a) Make an S-N plot (stress amplitude versus logarithm cycles to failure) using these data. (b) What is the fatigue limit for this alloy? (c) Determine fatigue lifetimes at stress amplitudes of 230 MPa (33,500 psi) and 175 MPa (25,000 psi). (d) Estimate fatigue strengths at 2 × 105 and 6 × 106 cycles.
A ul ? KBIS M 1:11 O photo_2021-0... -> 200 stress 150 (MPa) (00 50 0-2 strain From the tensile stress-strain behavior for the brass specimen d the diamcter is 12-8 mm Calculate the folluding:- 1- The Yield stress. 2- Modulus of elasticity. 3 - The Tensile strength . II
An NDT examination of a steel component reveals the presence of a 5 mm long edge crack. If plane - strain conditions prevail (KIC = 75 MPa.m0.5), what would be the residual service lifetime of the steel part if it were subjected to repeated stresses of 400 MPa? The Paris law equation for the steel has parameters of A=4X10-37 and m = 4
Part B The stress-strain diagram for a steel alloy having an original diameter of 1.0 in. and a gage length of 7 in. is shown in the figure below. (Eigure 1) Determine the load on the specimen that causes yielding. Express your answer to three significant figures and include appropriate units. HA Py- Value Units Submit Request Answer Part C Figure t oft> Determine the ultimate load the specimen will support. Express your answer to three significant figures and include appropriate units. NO 70 60 50 P. - Value Units 40 30 20 Submit Bequest Answer 10 (in/in) o G04 0m 12 016 020 024 02 a aa omams Provide Feedback
1. What is the approximate ductility (%EL) of a cold worked brass that has a yield strength of 345 MPa (50,000 psi) 140 120 1040 Steel 1040 Steel 120 700 600 100 500 Brass Brass eo S400 Brass 300 Copper 40 200 Copper 040 e 00 40 Copper 100 O 10 20 30 40 50 60 70 Percent cold work 200 0 10 20 30 40 50 60 70 Percent cold work O 10 20 30 40 D0 60 70 Percent cold work (a) (b)